Tensile Strength at Break for ABS Resin

Tensile Strength at Break for ABS Resin:

APPLICATION

l          Tape recorders

l          Video cassettes

l          Clocks

l          Office equipment

l          House-ware

Properties

Test

Test Condition

SI unit

English unit

Unit

s.p.

Unit

s.p.

Specific Gravity

ASTMD792

 

1.04

Melt Flow Index

ASTMD1238

200℃,5kgload

g/10min

2.0

Melt Flow Index

ASTMD1238

220℃,10kgload

g/10min

20.0

 

 

Mechanical

 

Izod Impact Strength

ASTMD256

23℃, 1/2 innotched

kg-cm/cm

17

ft-lb/in

3.1

Izod Impact Strength

ASTMD256

23℃, 1/8 innotched

kg-cm/cm

20

ft-lb/in

3.7

Tensile Strength at Yield

ASTMD638

23℃, 1/8 in,5 mm/min

kg/cm2

430

psi

6100

Tensile Strength at Break

ASTMD638

23℃, 1/8 in,5 mm/min

kg/cm2

360

psi

5100

Elongation at Break

ASTMD638

23℃, 1/8 in,5 mm/min

%

30

Flexural Yield

ASTMD790

23℃,2.8 mm/min

kg/cm2

750

psi

10700

Flexural Modulus

ASTMD790

23℃,2.8 mm/min

kg/cm2

26000

psi

370000

 

 

Thermal

 

Heat Distortion Temperature

ASTMD648

Unannealed, 1/2 in, 18.56 kg/cm2 load pressure

℃

83

℉

181

Vicat Softening Temperature

ASTMD1525

1/8 in,1 kgload

℃

103

℉

217

 

 

Physical

 

Rockwell Hardness

ASTMD785

23℃, R-scale

R-scale

115

Mold Shrinkage

ASTMD955

 

%

≦0.4

Water Absorption

ASTMD570

 

wt %

≦0.3

 

 

Flammability

UL-94

1/16 in

File No E50263

HB

 

 

Electrical

 

Relative Temperature Index

UL-764B

0.062 inabove

℃

60

℉

140

Hot Wire Ignition

UL-764A

0.062 inabove

Secs

18

High Current Arc Ignition

UL-764A

0.062 inabove

Arcs

200

Arc Tracking Rate

UL-764A

0.062 inabove

in/min

0